Optical and Dielectric Properties for the Determination of Gap States of the Polymer Conductor: Polypyrrol
International Journal of Optic and Photonic Engineering
Volume 5, Issue 2
Research Article DOI: 10.35840/2631-5092/4525
Optical and Dielectric Properties for the Determination of Gap States of the Polymer Conductor: Polypyrrol
C Belabed, A Tab, B Belhamedi and N Benrakaa
Table of Content
Figure 1: Extinction coefficient and Refractive index....
Extinction coefficient and Refractive index against wavelength for PPy.
Figure 2: Real and imaginary parts of the dielectric.....
Real and imaginary parts of the dielectric constant as function of photon energy of PPy.
Figure 3: Dependence of the dissipation factor....
Dependence of the dissipation factor tan δ on the photon energy for PPy.
Figure 4: Dependence of the dielectric relaxation time....
Dependence of the dielectric relaxation time τ on the photon energy hν. Inset: The εr vs. λ2.
Figure 5: Plot of n2 versus λ2 of PPy....
Plot of n2 versus λ2 of PPy.
Figure 6: Optical and electric conductivity against....
Optical and electric conductivity against photon energy for PPy.
Figure 7: Direct optical transitions of...
Direct optical transitions of PPy.
Figure 8: Indirect optical transitions...
Indirect optical transitions of PPy.
- R Kandulna, R Choudhary (2017) Robust electron transport properties of PANI/PPY/ZnO polymeric nanocomposites for OLED applications. Optik 144: 40-48.
- M Majhi, R Choudhary, P Maji (2017) HCl protonated polymeric PANI-ZnS nanocomposites and measurement of their robust dielectric, optical and thermal performance. Optik 136: 181-191.
- S Krishnaswamy, V Ragupathi, S Raman, P Panigrahi, G Nagarajan (2019) Optical properties of P- type polypyrrole thin film synthesized by pulse laser deposition technique: Hole transport layer in electroluminescence devices. Optik 194: 163034.
- S Sharma, S Misra (2002) Optimization of conducting polymer thin film optical and electrical waveguides. Optik 113: 351-353.
- A Alyamani, K Ibnaouf, O Yassin, M AlSalhi, Z Fekkai, et al. (2016) Spectral, electrical and morphological properties of spin coated MEH-PPV and cresyl violet blended thin films for a light emitting diode. Optik 127: 2331-2335.
- N Mustapha, Z Fekkai, A Alkaoud (2016) Enhanced efficiency of organic solar cells based on (MEH-PPV) with graphene and quantum dots. Optik 127: 2755-2760.
- C Belabed, N Haine, Z Benabdelghani, B Bellal, M Trari (2014) Photocatalytic hydrogen evolution on the hetero-system polypyrrol/TiO2 under visible light. Int J Hydrogen Energy 39: 17533-17539.
- C Belabed, G Rekhila, M Doulache, B Zitouni, M Trari (2013) Photo-electrochemical characterization of polypyrrol: Application to visible light induced hydrogen production. Sol Energy Mater Sol Cells 114: 199-204.
- A Ashery, MA Salem, A Farag (2018) Optical and electrical performance of ploypyrrol thin films and its hybrid junction applications. Optik 172: 302-310.
- J Chandrasekaran, D Nithyaprakash, B Punithaveni, L Sasikumar, KB Ajjan, et al. (2013) Study of optical, dielectric and optoelectronic properties of dodecylbenzene sulfonic acid doped polypyrrole. Optik 124: 2057-2061.
- Sk Basha, G Sundari, K Kumar, K Rao, MC Rao (2018) Preparation and characterization of ruthenium based organic composites for optoelectronic device application. Optik 164: 596-605.
- C Belabed, B Bellal, A Tab, K Dib, M Trari (2018) Optical and dielectric properties for the determination of gap states of the polymer semiconductor: Application to photodegradation of organic pollutants. Optik 160: 218-226.
- Z Serbetc, HM El-Nasser, F Yakuphanoglu (2012) Photoluminescence and refractive index dispersion properties of ZnO nanofibers grown by sol-gel method. Spectrochimica Acta Part A: Molecular and Biomolecular Spectroscopy 86: 405-409.
- P Dinakaran, S Kalainathan (2013) Studies on the optical and mechanical properties of organic nonlinear optical 1-(4-fluorostyryl)-4-nitrostilbene (FNS) single crystal. Optik 12: 5111-5115.
- GB Sakr, IS Yahia, M Fadel, SS Fouad, N Romcevic (2010) Optical spectroscopy, optical conductivity, dielectric properties and new methods for determining the gap states of CuSe thin films. J Alloy Compd 507: 557-562.
- MM El-Nahassa, AAM Faraga, EM Ibrahim, S Abd-El-Rahman (2004) Structural, optical and electrical properties of thermally evaporated Ag2S thin films. Vacuum 72: 453-460.
- N Doufar, M Benamira, H Lahmar, M Trari, I Avramova, et al. (2020) Structural and photochemical properties of Fe-doped ZrO2 and their application as photocatalysts with TiO2 for chromate reduction. J Photochem Photobiol A: Chem 386: 112105.
C Belabed1*, A Tab2, B Belhamedi3 and N Benrakaa1
1Laboratory of Materials Physic, Faculty of Physic, USTHB, Algiers, Algeria
2Laboratory of Chromatography, Faculty of Chemistry, USTHB, Algiers, Algeria
3Laboratory of Physical and Chemical Study of Materials and Applications in the Environment, Faculty of Chemistry, USTHB, Algiers, Algeria
C Belabed, Laboratory of Materials Physic, Faculty of Physic, USTHB, BP 32 El-Alia, 16111, Algiers, Algeria, Tel: +213-21-24-79-55, Fax: +213-21-24-80-08.
Accepted: August 26, 2020 | Published Online: August 28, 2020
Citation: Belabed C, Tab A, Belhamedi B, Benrakaa N (2020) Optical and Dielectric Properties for the Determination of Gap States of the Polymer Conductor: Polypyrrol. Int J Opt Photonic Eng 5:025
Copyright: © 2020 Belabed C, et al. This is an open-access article distributed under the terms of the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original author and source are credited.
The polypyrrole is a conducting polymer prepared by chemical route. The diffuse reflectance measured in the wavelength range (300-2500 nm) permitted to calculate the refractive index (n), extinction coefficient (k), dissipation factor (tan δ) and relaxation time (τ). The optical band gap (Eg) was evaluated from the dielectric and conductivity properties, its value (1.01 eV) was confirmed by using the Tauc relation.
Polymer conductor, Polypyrrol, Optical dispersion parameters, Dielectric properties, Optical constants
The development of electronic devices light, flexible also small-size and rechargeable has increased during recent years [1-3]. In this respect, the polymer conductors have attracted a great interest from both academic and technical point of view over the last decade [4-6]. Such materials not only work in a similar way to inorganic semi-conductors (SCs) but also have additional advantages like environmental friendliness, facile synthesis and light weight . Moreover, organic materials show higher conductivity due to the itinerant electron on conjugated system compared to the inorganic SCs . The main advantage with organic materials is that both the structure and properties can be talloried, with inherent ultra-fast time and large optical susceptibilities, needed characteristics of the modern technological requirements .
Among the candidates, Polypyrrol (PPy) is an emergent material because it has interesting optical properties  which are essential for optoelectronic applications . The optical constants of the semiconductors play an important from both a fundamental and technological points of view. The refractive index is closely related to the electronic polarizability of ions and local field inside the materials . With this in mind, we have prepared PPy by chemical route and investigated the optical and dielectric properties.
The polypyrrol (PPy) was prepared by chemical route, from the pyrrole monomer which was purified to remove the impurities. The distilled pyrrole (0.2 M) was dissolved in a mixture of water/ethanol (1:1), FeCl3 (0.1 M) was slowly added to the solution under stirring for 24 h at room temperature. The black precipitate PPy was filtered, thoroughly washed with water and ethanol mixture and dried at 323 K for 24 h under vacuum.
Results and Discussion
Refractive index dispersion
The reflectance measurement of PPy was used for determination of the refractive (n) and extinction (k) indices using the complex optical refraction :
While the refractive index is determined by the relation :
Figure 1 shows the variations of n and k versus the wavelength (λ), in the UV- visible region, the coefficient k increases drastically to reach a maximum at 760 nm and this indicates that a large fraction of the light is lost. On the other hand, the refractive index n decreases with increasing λ indicating a best optical characteristic of PPy with promising applications in the visible region. Above which k decreases up to 1600 nm and remains nearly constant and this indicates a maximum light absorption in the IR region (λ > 760 nm). While for the refractive index increases, and its value has doubled in the IR region.
The interaction electron/photon is expressed by the complex dielectric constant (ε) which is proportional to the polarizability of PPy and comprises the real (εr) and imaginary parts (εi), they are determined from the coefficients n and k by using the following relations :
The dependence of εr and εi versus hν are illustrated in Figure 2. The extrapolation of the straight line to the real and imaginary curves of the dielectric constant to the x-axis yields an optical gap Egof ~ 0.6 eV.
In physics, the measurement of loss-rate of power of a mechanical mode in oscillation is expressed by the dissipation factor. In polymer conductors, the electrical power lost in the form of heat and the dissipation factor is given by the following relation :
Figure 3 shows the profile tan δ vs. hν. In the range (0.3-1.4 eV), tan δ increases significantly indicating a radiative motor effect and this means that the radiative effect dominates the developed physics. By contrast, tan δ decreases above 1.4 eV and this implies that the energies are suitable, in agreement with the k values. Different quantities were used to characterize the optical properties of PPy among which the dielectric relaxation time (τ), evaluated from the relation :
Where ε∞ is the infinite dielectric constant which can be easily deduced when the incident-energy tends to infinity, and is the smallest value of εr (ε∞ = 1.54) (Figure 4 insert). Figure 4 shows the dielectric relaxation time as a function of hν for PPy. The cross-point between the tangent of the plot of lower and higher values of the energy (hν) of the calculated relaxation time to the x-axis. Permit to evaluate the band-to-band absorption, which corresponds to the optical bandgap (Eg ~ 1 .01 eV).
The relation between the coefficient (n) and lattice dielectric constant (εL) is given by :
Where, e is the electronic charge and c is the velocity of light and N/m* the ratio of the carriers concentration to the effective mass. The plot n2 versus λ2 (Figure 5) is linear in conformity with Eq. (8). The εL values (1.57) can be easily deduced by extrapolating the plots to λ2 = 0 while the ration N/m* is determined from the slope of the graph. The values of ε∞ and εL are close to each due to no carrier contribution.
Optical and electrical conductivity
Figure 6 shows graphs the σopt and σe as a function of (hν). At first sight, σe decreases with increasing the energy hν, and σopt increases with augmenting the photon energy. The peak at 1.72 eV this implies that PPy has good optical properties in the visible region and the conduction of photons is a dominant mechanism instead of the electrical conduction. The cross-point between the curves σopt and σe allows evaluating the optical band gap Eg (∼ 0.95 eV) in good agreement with our previous results .
Determination of the optical band gap
The relation between the absorption coefficient (α) and incident photon energy (hν) provides valuable information about the optical gap by using the relation :
The exponent m depends on the transition type, m = 2 and 1/2 for direct or indirect transitions respectively. The intercepts of the linear plot (αhν)m with the hν-axis of PPy yield, direct and indirect transitions at 0.42 and 1.01 eV respectively (Figure 7 and Figure 8), in good agreement with the values obtained previously. The study has been the subject of continuing interest on the hero-system PPy/TiO2; the results are satisfactory and the work will be published in a near future.
The polypyrrol was prepared by chemical route, and the electric and dielectric properties were investigated. The peak in the spectral distribution of the refractive index and the dielectric relaxation time corresponds to the fundamental absorption edge. The optical band gap was evaluated by different methods, the obtained values are almost close to that determined by diffuse reflectance.
The authors wish to express their thanks for the financial support from the Directorate general of Scientific Research and technological Development (DGRST, Algeria).